What is a bimetallic screw barrel made of?

A bimetallic screw barrel combines a steel base with a separate wear-resistant alloy layer bonded to the working surfaces. Common base steels include 38CrMoAlA, 34CrAlNi7, 31CrMoV9, and 42CrMo. The alloy layer on screws is typically Ni60, Colmonoy 56, or Colmonoy 83, applied by PTA welding at 1.0 to 1.5 mm thickness. The alloy layer inside barrels is a nickel- or iron-based casting alloy, applied by centrifugal casting at 2.0 to 3.0 mm. The two materials stay in distinct layers with a metallurgical bond between them.

How much longer does a bimetallic screw barrel last than nitrided?

Long enough to matter on abrasive compounds, and not long enough to matter on clean ones. On glass-filled, mineral-filled, or recycled feed, the difference in service life is substantial, because the nitride case is only 0.4 to 0.7 mm deep while bimetallic gives 1.0 to 1.5 mm on the screw and 2.0 to 3.0 mm in the barrel, in a harder and more chemically resistant material. On clean unfilled resin, both constructions can run for years and the upgrade earns little. Any supplier quoting a fixed multiplier without asking what you process is guessing.

Is a bimetallic screw barrel the same as a chrome-plated one?

No. Chrome plating deposits a thin layer on the surface, which can flake off under thermal cycling and mechanical load. Bimetallic construction fuses several millimeters of alloy to the base steel through welding or casting, so the layer becomes part of the component and cannot peel. Chrome plating serves specific purposes such as release and mild corrosion protection, but it is not a wear solution for abrasive compounds.

Can a bimetallic screw be repaired when it wears out?

Yes, in many cases. A worn bimetallic screw can be re-welded with fresh PTA hardfacing and re-machined back to original geometry. A worn barrel bore can be re-bored and re-lined by centrifugal casting. Refurbishment keeps the original shaft, keyway, journal, and housing, which often makes it the economical route when the OEM part is discontinued or the lead time is long. Send photos and wear measurements to get a refurbish-or-replace assessment.

Do I need bimetallic for the screw, the barrel, or both?

Both, in most cases, because they wear as a pair. Clearance between the flight lands and the bore is a system property. A new bimetallic screw inside a worn oversized bore still runs at enlarged clearance, so output stays low and the new screw wears against an irregular surface. If you are upgrading one, measure the other. Replacing only half the wear pair transfers the problem to the new part.

Does a bimetallic screw barrel work for PVC?

Yes, but the alloy grade matters more than the label. Rigid PVC is a corrosion problem before it is an abrasion problem, because the polymer releases hydrogen chloride as it degrades. That means you want a corrosion-led alloy: Ni60 or Colmonoy 56 on the screw, and EJS02 or EJS03 in the barrel. A tungsten-carbide grade like Colmonoy 83 is built for abrasion and is not the right answer for PVC unless the compound carries heavy filler as well.

What is the temperature limit of a bimetallic barrel?

It depends on the casting alloy, and it ranges from about 400 to 600 degrees Celsius. EJS01 is rated to about 400. EJS02 and EJS03 reach about 450. EJS04, the tungsten carbide grade, tolerates up to about 600. If your process runs hot, the temperature limit becomes a gating specification, so tell your manufacturer the actual zone temperatures rather than the design values.

Can EJS supply bimetallic screw barrels for my machine?

Yes. EJS manufactures bimetallic screws and barrels in-house, with PTA-welded hardfacing on screws and centrifugally cast lining in barrels, for single screw, parallel twin, conical twin, injection molding, and rubber geometries. Parts are built per drawing or reverse-engineered from the machine model and code when no drawing exists. Quotation follows within one working day once the specification is clear.

ຖັງ Screw Bimetallic ແມ່ນຫຍັງ? ໂລຫະປະສົມ & ເວລາທີ່ຈະຊື້

ທີມງານວິຊາການ EJS· ກໍລະກົດ 2026 · ບັນທຶກວິສະວະກໍາພາກສະຫນາມ

A ຖັງ screw bimetallicປະກອບດ້ວຍຊັ້ນໂລຫະປະສົມທີ່ທົນທານຕໍ່ການສວມໃສ່ແຍກຕ່າງຫາກທີ່ຜູກມັດດ້ວຍໂລຫະປະສົມກັບຖານເຫຼັກ - ບໍ່ແມ່ນການເຄືອບ, ບໍ່ແມ່ນການເຄືອບ. Screws ໄດ້ຮັບ PTA-welded hardfacing ຢູ່ 1.0-1.5 ມມ. ຖັງມີເສັ້ນຜ່າສູນກາງ 2.0–3.0 ມມ. ການອັບເກຣດຈະມີລາຍໄດ້ຄ່າໃຊ້ຈ່າຍຂອງມັນຕໍ່ກັບສານຂັດ ຫຼືສານກັດກ່ອນ, ແລະເສຍເງິນໃຫ້ກັບຢາງທີ່ສະອາດທີ່ບໍ່ໄດ້ເຕີມເຕັມ.

ສະກູຈະມາຮອດໂຮງງານຂອງພວກເຮົາກັບເຮືອບິນບິນໄດ້ອ້ອມຮອບໄປ. ລູກຄ້າແລ່ນ nylon ແກ້ວ 30%. ສະກູແມ່ນ nitrided. ມັນໃຊ້ເວລາສິບສີ່ເດືອນ.

ເລຂາຄະນິດດຽວກັນໃນການກໍ່ສ້າງ bimetallic, ໃນປະສົມດຽວກັນ, ກັບຄືນມາສໍາລັບການກວດກາປີຕໍ່ມາແລະຍັງວັດແທກຄວາມທົນທານ.

ຊ່ອງຫວ່າງນັ້ນແມ່ນສິ່ງທີ່ barrel screw bimetallic ຊື້. ແຕ່ຊ່ອງຫວ່າງມີພຽງແຕ່ຍ້ອນວ່າສານປະສົມແມ່ນຂັດ. ແລ່ນ PE ທີ່ສະອາດຜ່ານສະກູທັງສອງແລະເຈົ້າຈະພະຍາຍາມບອກພວກເຂົາແຍກກັນໃນຕອນທ້າຍຂອງຊີວິດ - ແລະເຈົ້າຈະຕ້ອງເສຍເງິນໃນການຍົກລະດັບ.

ຄູ່ມືນີ້ອະທິບາຍວ່າການກໍ່ສ້າງ bimetallic ແມ່ນຫຍັງ, ມັນຖືກຜະລິດແນວໃດ (ສອງຂະບວນການທີ່ແຕກຕ່າງກັນ, ເຊິ່ງບົດຄວາມສ່ວນໃຫຍ່ຜິດພາດ), ລະດັບໂລຫະປະສົມທີ່ມີຄວາມສໍາຄັນ, ແລະ - ສ່ວນທີ່ບໍ່ມີໃຜຂຽນ - ເມື່ອການຍົກລະດັບແມ່ນເສຍງົບປະມານຂອງທ່ານ.

ຄໍາຕອບດ່ວນ

Bimetallicໝາຍເຖິງຊັ້ນໂລຫະປະສົມທີ່ທົນທານຕໍ່ການສວມໃສ່ຂອງໂລຫະປະສົມກັບຖານເຫຼັກ — ບໍ່ແມ່ນການເຄືອບ, ບໍ່ແມ່ນການເຄືອບ.
Screw ແລະ barrel ແມ່ນເຮັດແຕກຕ່າງກັນ.Screws ໄດ້ຮັບ PTA-welded hardfacing (1.0-1.5 ມມ). ຖັງເກັບມ້ຽນດ້ວຍເສັ້ນຜ່າສູນກາງ (2.0–3.0 ມມ).
ຊື້ມັນເມື່ອສານປະສົມຂອງເຈົ້າຖືກຂັດຫຼືກັດກ່ອນ:ເສັ້ນໃຍແກ້ວ, ເຄື່ອງຕື່ມແຮ່ທາດ, ຕ້ານໄຟ, PVC ແຂງ, ອາຫານທີ່ລີໄຊເຄີນ.
ຂ້າມມັນໄປສໍາລັບນ້ໍາຢາງທີ່ສະອາດ.Nitrided handles ທໍາມະຊາດ PP, PE, PS, ແລະ ABS ໃນສ່ວນຫນຶ່ງຂອງຄ່າໃຊ້ຈ່າຍ.
ຊັ້ນຮຽນແມ່ນສໍາຄັນຫຼາຍກ່ວາຄໍາ.ຂໍຊື່ຊັ້ນຮຽນ, ຄວາມຫນາຂອງຊັ້ນ, ແລະຄວາມແຂງ.

1. Bimetallic Screw Barrel ແມ່ນຫຍັງ?

ຖັງສະກູ bimetallic ປະສົມປະສານສອງໂລຫະທີ່ເຮັດສອງວຽກທີ່ແຕກຕ່າງກັນ. ເຫຼັກພື້ນຖານສະຫນອງຄວາມເຂັ້ມແຂງໂຄງສ້າງ, ຄວາມຕ້ານທານ fatigue, ແລະສະຖຽນລະພາບມິຕິລະດັບ. ຊັ້ນໂລຫະປະສົມແຍກຕ່າງຫາກ, ຜູກມັດກັບພື້ນຜິວທີ່ເຮັດວຽກ, ສະຫນອງການຕໍ່ຕ້ານການສວມໃສ່ແລະການຕໍ່ຕ້ານ corrosion ຕາມຄວາມຕ້ອງການຂອງໂພລີເມີ.

"Bi" ຫມາຍຄວາມວ່າສອງ. ທັງສອງໂລຫະແມ່ນfused, ບໍ່ປະສົມ. ການປະສົມຂອງໂລຫະແມ່ນໂລຫະປະສົມ; ພາກສ່ວນ bimetallic ຮັກສາສອງວັດສະດຸຂອງມັນຢູ່ໃນຊັ້ນທີ່ແຕກຕ່າງກັນໂດຍມີໂລຫະປະສົມລະຫວ່າງພວກມັນ.

ຄວາມແຕກຕ່າງນັ້ນມີຄວາມສໍາຄັນທາງດ້ານການຄ້າ. ຖັງທີ່ເຮັດດ້ວຍ chrome-plated ບໍ່ແມ່ນ bimetallic — ແຜ່ນແມ່ນຕັ້ງຢູ່ພື້ນຜິວແລະສາມາດ flake ໄດ້. ຖັງ nitrided ບໍ່ແມ່ນ bimetallic - nitriding ກະຈາຍໄນໂຕຣເຈນເຂົ້າໄປໃນເຫຼັກທີ່ມີຢູ່ແລ້ວແທນທີ່ຈະເພີ່ມວັດສະດຸໃຫມ່. ກຖັງ screw bimetallicເພີ່ມໂລຫະປະສົມທີ່ແທ້ຈິງ, ຫນາຫຼາຍ millimeters, ທີ່ຈະກາຍເປັນສ່ວນຫນຶ່ງຂອງອົງປະກອບ.

Bimetallic screw barrel manufactured by EJS with hardfaced screw flights and alloy-lined barrel bore

ເຫຼັກກ້າພື້ນຖານ

ເຫຼັກພື້ນຖານທີ່ໃຊ້ພາຍໃຕ້ຊັ້ນໂລຫະປະສົມ. ໃນສ່ວນທີ່ສ້າງຂຶ້ນຢ່າງຖືກຕ້ອງ, ເຫຼັກພື້ນຖານບໍ່ເຄີຍແຕະໂພລີເມີ.
ເຫຼັກພື້ນຖານ	ມາດຕະຖານ	ບ່ອນທີ່ມັນຖືກນໍາໃຊ້
38CrMoAlA	1.8509	ເຫຼັກ nitriding ຂອງ workhorse ໃນທົ່ວອາຊີ
34CrAlNi7	1.8550	Nitrides ເລິກກວ່າ ແລະຍາກກວ່າ 38CrMoAlA
31CrMoV9	1.8519	ມີຄວາມເຂັ້ມແຂງສູງ, ທົນທານຕໍ່ຄວາມເມື່ອຍລ້າທີ່ດີ
42CrMo	AISI 4140	ຍາກ, ສາມາດໃຊ້ໄດ້ຢ່າງກວ້າງຂວາງ
SKD61 / SS316	—	ອຸນຫະພູມສູງແລະຫນ້າທີ່ສໍາຄັນ corrosion

2. ສອງຂະບວນການທີ່ແຕກຕ່າງກັນ: Screw vs Barrel

ນີ້ແມ່ນບ່ອນທີ່ບົດຄວາມສ່ວນໃຫຍ່ກ່ຽວກັບຫົວຂໍ້ນີ້ຜິດພາດ. ພວກເຂົາເຈົ້າອະທິບາຍ barrels screw bimetallic ເປັນຖ້າຫາກວ່າຂະບວນການຫນຶ່ງເຮັດໃຫ້ທັງສອງພາກສ່ວນ. ສອງຂະບວນການທີ່ແຕກຕ່າງກັນຢ່າງສິ້ນເຊີງແມ່ນມີສ່ວນຮ່ວມ, ແລະການຮູ້ວ່າອັນໃດທີ່ບອກທ່ານວ່າຜູ້ສະຫນອງຕົວຈິງແມ່ນຜະລິດຢູ່ໃນເຮືອນ.

Screw: ການເຊື່ອມ PTA (Hardfacing)

PTA ຫຍໍ້ມາຈາກplasma ໂອນ arc. ໄຟ plasma ເຮັດ ໃຫ້ ຝຸ່ນ ຂອງ ໂລ ຫະ ລະ ລາຍ ແລະ ຝາກ ມັນ ໃສ່ ດິນ ບິນ screw ເປັນ bead ການ ເຊື່ອມ. ໂລຫະປະສົມທີ່ຝາກໄວ້ຈະເຊື່ອມໂລຫະດ້ວຍເຫຼັກພື້ນຖານ - ນີ້ແມ່ນການເຊື່ອມ, ບໍ່ແມ່ນສີດ.

ຫຼັງຈາກການເຊື່ອມໂລຫະ, ສະກູກັບຄືນໄປຫາເຄື່ອງກຶງ. ຄວາມແຂງກະດ້າງຂະໜາດໃຫຍ່ຖືກເຄື່ອງຈັກລົງໄປຫາເລຂາຄະນິດຂອງຖ້ຽວບິນສຸດທ້າຍ ແລະຄວາມທົນທານ. ສິ່ງທີ່ຍັງເຫຼືອແມ່ນ ກ1.0 ຫາ 1.5 ມມຊັ້ນຂອງໂລຫະປະສົມທີ່ທົນທານຕໍ່ການສວມໃສ່ໃນບ່ອນທີ່ສະກູແຕະໃສ່ຝາຖັງ. ພື້ນທີ່ຂອງການບິນແມ່ນບ່ອນທີ່ screw wears ອອກ, ສະນັ້ນ hardfacing ໃຫ້ເຂົາເຈົ້າແມ່ນຈຸດທັງຫມົດ.

PTA hardfacing alloy welded onto extruder screw flight lands at the EJS workshop — Hardfacing ໃນທີ່ດິນການບິນ. ໂລຫະປະສົມໄດ້ຖືກເຊື່ອມໂລຫະ oversize, ຫຼັງຈາກນັ້ນ machined ກັບຄືນໄປບ່ອນເລຂາຄະນິດການບິນສຸດທ້າຍ - ເບິ່ງຂອງພວກເຮົາຫນ້າ screw hardfacing.

The Barrel: ການຫລໍ່ centrifugal

ເຈາະຖັງໄດ້ຮັບໂລຫະປະສົມຂອງຕົນໂດຍການຫລໍ່ centrifugal ຕາມແນວນອນ. ໂລຫະປະສົມ Molten ແມ່ນ poured ເຂົ້າໄປໃນຮ່າງກາຍ barrel spinning; ຜົນບັງຄັບໃຊ້ centrifugal ຖິ້ມມັນຕໍ່ກັບກໍາແພງພາຍໃນ, ບ່ອນທີ່ມັນແຂງຕົວເປັນຄວາມຫນາແຫນ້ນ, ແມ່ນແຕ່ lining. ການຫລໍ່ພາຍໃຕ້ບັນຍາກາດທີ່ມີການຄວບຄຸມຮັກສາ porosity ອອກແລະສຽງພັນທະນາການ.

ຜົນໄດ້ຮັບແມ່ນ ກ2.0 ຫາ 3.0 ມມໂລຫະປະສົມ lined ລົງຕາມຄວາມຍາວເຕັມ. ເປັນຫຍັງໜາກວ່າສະກູ? ເລຂາຄະນິດ ແລະ ເສດຖະສາດ. ຮູເຈາະແມ່ນພື້ນຜິວທີ່ສະກູແລ່ນຕ້ານກັບຄວາມຍາວທັງຫມົດ, ແລະຖັງມີລາຄາຖືກກວ່າທີ່ຈະປ່ຽນແທນສະກູ.

Bimetallic barrels with centrifugally cast alloy lining inside the bore, produced at EJS — ຖັງ Bimetallic. ເສັ້ນໂລຫະປະສົມແລ່ນຄວາມຍາວເຕັມ - ເບິ່ງຂອງພວກເຮົາໜ້າຖັງ bimetallic.

ທັງສອງຂະບວນການຂ້າງຄຽງ.
ອົງປະກອບ	ຂະບວນການ	ຊັ້ນໂລຫະປະສົມ	ສິ່ງທີ່ມັນປົກປ້ອງ
ໝວກ	ການເຊື່ອມໂລຫະ PTA (Hardfacing)	1.0 – 1.5 ມມ	ຖ້ຽວບິນລົງ — ດ້ານການຕິດຕໍ່ເລື່ອນ
ຖັງ	ການຫລໍ່ຈຸດສູນກາງ	2.0 – 3.0 ມມ	ເຈາະເຕັມ — ພື້ນຜິວທີ່ສະກູແລ່ນຕ້ານ

ການທົດສອບການປະຕິບັດສໍາລັບຜູ້ສະຫນອງ.ຂໍໃຫ້ພວກເຂົາອະທິບາຍວິທີການທີ່ເຂົາເຈົ້າໃຊ້ໂລຫະປະສົມກັບສະກູແລະວິທີການທີ່ເຂົາເຈົ້ານໍາໃຊ້ມັນໃສ່ຖັງ. ຜູ້ຜະລິດທີ່ແທ້ຈິງຊື່ສອງຂະບວນການທີ່ແຕກຕ່າງກັນໂດຍບໍ່ມີການລັງເລ. ບໍລິສັດການຄ້າໃຫ້ຄໍາຕອບທີ່ບໍ່ຊັດເຈນຫນຶ່ງກ່ຽວກັບ "ການເຄືອບ."

3. Bimetallic vs Nitrided: ສິ່ງທີ່ປ່ຽນແປງຕົວຈິງ

Nitriding ກະຈາຍໄນໂຕຣເຈນເຂົ້າໄປໃນຫນ້າດິນຂອງເຫລໍກ, ສ້າງເປັນກໍລະນີແຂງ. ບໍ່ມີການເພີ່ມວັດສະດຸໃຫມ່. ກໍລະນີແລ່ນ0.4 ຫາ 0.7 ມມເລິກ, ແລະພື້ນຜິວເຖິງປະມານ HV 850-950 ກ່ຽວກັບ 38CrMoAlA.

ກໍລະນີນັ້ນແມ່ນຍາກແທ້ໆ. ຈຸດອ່ອນຂອງມັນແມ່ນວ່າມັນບາງ, ແລະມັນຈໍາກັດທາງເຄມີ.

ການປຽບທຽບການກໍ່ສ້າງ. ກຖັງ screw nitridedບໍ່ແມ່ນຜະລິດຕະພັນຫນ້ອຍ - ມັນເປັນຫນ້າທີ່ທີ່ແຕກຕ່າງກັນ.
ຊັບສິນ	ໄນທຣິກ	Bimetallic
ປະເພດຊັ້ນ	ກໍລະນີແຜ່ກະຈາຍ (ບໍ່ມີວັດສະດຸເພີ່ມ)	ເພີ່ມໂລຫະປະສົມ, ຜູກມັດດ້ວຍໂລຫະ
ຄວາມເລິກຂອງຊັ້ນ Screw	0.4 – 0.7 ມມ	1.0 – 1.5 ມມ
ຄວາມເລິກຂອງຊັ້ນຖັງ	0.4 – 0.7 ມມ	2.0 – 3.0 ມມ
ຄວາມແຂງຂອງພື້ນຜິວ	HV 850 – 950	HRC 50 – 62 (ຂຶ້ນກັບເກຣດ)
ທົນທານຕໍ່ການຂັດ	ປານກາງ	ສູງເຖິງດີເລີດ
ຄວາມຕ້ານທານຕໍ່ການກັດກ່ອນ	ຈຳກັດ	ດີກັບດີເລີດ (ຂຶ້ນກັບຄະແນນ)
ຄ່າໃຊ້ຈ່າຍທີ່ກ່ຽວຂ້ອງ	1.0×	ສູງຂຶ້ນ - ໂລຫະປະສົມ ແລະຂະບວນການທັງສອງເພີ່ມຄ່າໃຊ້ຈ່າຍ
ຫນ້າທີ່ທີ່ດີທີ່ສຸດ	ສະອາດ, ຢາງບໍ່ເຕັມ	ອາຫານທີ່ເຕີມເຕັມ, corrosive, ຫຼື recycled feed

ເມື່ອສານເຕີມເຕັມທີ່ມີຮອຍຂີດຂ່ວນຕັດຜ່ານກໍລະນີ nitride, ເຫລໍກຫຼັກທີ່ອ່ອນກວ່າຈະຢູ່ໃຕ້ແລະ erodes ໄວ. ນັ້ນແມ່ນເຫດຜົນທີ່ວ່າຊິ້ນສ່ວນ nitrided ໃນທາດປະສົມທີ່ເຕັມໄປດ້ວຍແກ້ວບໍ່ຍ່ອຍສະຫຼາຍຢ່າງສະຫງ່າງາມ - ພວກມັນຍຶດ, ຫຼັງຈາກນັ້ນລົ້ມເຫລວຢ່າງໄວວາ.

ຊັ້ນ bimetallic ມີຄວາມເລິກ millimeters. ມັນອ່ອນລົງຢ່າງຊ້າໆ, ແລະອັດຕາການສວມໃສ່ຢູ່ປະມານເສັ້ນຊື່. ຄວາມເລິກນັ້ນແມ່ນບ່ອນທີ່ຄວາມຕ້ານທານການສວມໃສ່ຢູ່ - ແລະມັນແມ່ນເຫດຜົນທີ່ວ່າຊີວິດການບໍລິການຂອງທາດປະສົມຂັດຈະແຍກອອກຢ່າງຫຼວງຫຼາຍລະຫວ່າງສອງການກໍ່ສ້າງ.

4. ເກຣດໂລຫະປະສົມ — ຖາມຫາຈໍານວນ

ຜູ້ສະຫນອງສ່ວນໃຫຍ່ອະທິບາຍໂລຫະປະສົມຂອງພວກເຂົາເປັນ "nickel-based" ຫຼື "tungsten carbide." ນັ້ນບອກເຈົ້າເກືອບບໍ່ມີຫຍັງເລີຍ. Ni60 ແລະ Colmonoy 83 ທັງສອງແມ່ນອີງໃສ່ nickel, ແລະພວກເຂົາປະຕິບັດແຕກຕ່າງກັນຫຼາຍ.

Screw Hardfacing Alloys (PTA-welded)

ໂລຫະປະສົມ	ອົງປະກອບ	ຕ້ານການສວມໃສ່	ຕ້ານການກັດກ່ອນ	ຄວາມແຂງ
Ni60	Ni+Cr+Fe+Si	★★★	★★★★	HRC 56–62
ໂຄໂມໂນຍ 56	Ni+Cr+Si+Fe	★★★	★★★★	HRC 53–58
ໂຄໂມໂນຍ 83	Ni+Wc+Cr+C	★★★★	★★★★	HRC 50–55

Barrel Casting Alloys (Centrifugally Casting)

ໂລຫະປະສົມ	ອົງປະກອບ	ຕ້ານການສວມໃສ່	ຕ້ານການກັດກ່ອນ	ຄວາມແຂງ	ອຸນຫະພູມສູງສຸດ
EJS01	Fe+Ni+Cr+B	★★★	★★	HRC 58–62	≤ 400°C
EJS02	Ni+Cr+Co+B	★★	★★★	HRC 50–58	≤ 450°C
EJS03	Ni+Cr+Co+V+B	★★★	★★★	HRC 55–60	≤ 450°C
EJS04	Ni+Wc+Cr+B	★★★★	★★★	HRC 55–60	≤ 600°C

Bimetallic screw with nickel-based hardfacing alloy on the flight lands, made by EJS — ສະກູ bimetallic ສໍາເລັດຮູບ. ໂລຫະປະສົມອັນໃດຢູ່ໃນດິນແດນເຫຼົ່ານັ້ນ — Ni60, Colmonoy 56, ຫຼື Colmonoy 83 — ແມ່ນຂໍ້ມູນຈໍາເພາະທີ່ຕັດສິນໃຈຊີວິດການບໍລິການ.

ລາຍລະອຽດທີ່ພາຄົນຂຶ້ນ

ເບິ່ງ Colmonoy 83. ຄວາມແຂງຂອງມັນອ່ານHRC 50–55 — ຕ່ໍາກວ່າຫຼາຍກວ່າ Ni60 ຢູ່ HRC 56–62. ແຕ່ Colmonoy 83 ມີການຈັດອັນດັບຕ້ານການສວມໃສ່.

ຄວາມແຂງກະດ້າງແລະຄວາມທົນທານຕໍ່ການຂັດບໍ່ແມ່ນຊັບສິນດຽວກັນ. ຄວາມແຂງຂອງພື້ນຜິວສູງຕ້ານການ indentation; ການຕໍ່ຕ້ານການສວມໃສ່ກັບເຄື່ອງຕື່ມ abrasive ແມ່ນມາຈາກ particles carbide ຝັງຢູ່ໃນໂລຫະປະສົມ. Colmonoy 83 ປະຕິບັດ tungsten carbide ("Wc" ໃນອົງປະກອບຂອງມັນ). ອະນຸພາກ carbide ຝັງເຫຼົ່ານັ້ນເຮັດວຽກຕ້ານເສັ້ນໃຍແກ້ວ, ແຮ່ທາດ, ແລະ grit ໃນ recyclate, ແລະ matrix ອ້ອມຂ້າງເຂົາເຈົ້າສາມາດ softer ໂດຍບໍ່ມີການທໍາຮ້າຍຜົນໄດ້ຮັບ.

ດັ່ງນັ້ນເມື່ອຜູ້ສະຫນອງອ້າງເຖິງຄວາມແຂງຂອງທ່ານຢ່າງດຽວ, ພວກເຂົາກໍາລັງອ້າງອີງຕົວເລກທີ່ບໍ່ຖືກຕ້ອງ. ຮ້ອງຂໍໃຫ້ມີອົງປະກອບ.

ການຈັບຄູ່ຊັ້ນຮຽນກັບສານປະກອບ

ທາດປະສົມຂອງເຈົ້າ	Screw Alloy	Barrel Alloy	ເປັນຫຍັງ
ເສັ້ນໃຍແກ້ວແກ້ວ, ເຕັມໄປດ້ວຍແຮ່ທາດ	ໂຄໂມໂນຍ 83	EJS01 ຫຼື EJS04	Tungsten carbide ຈັດການກັບການຂັດ
PVC ແຂງ	Ni60 ຫຼື ໂຄໂມໂນຍ 56	EJS02 ຫຼື EJS03	ການກັດກ່ອນຂອງ HCl, ບໍ່ແມ່ນການຂັດ
ລີໄຊເຄີນ / ອາຫານຫຼັງຜູ້ບໍລິໂພກ	ໂຄໂມໂນຍ 83	EJS01 ຫຼື EJS04	ການປັບດິນຈີ່ ແລະໂລຫະເຮັດໜ້າທີ່ຄືກັບເຈ້ຍຊາຍ
ທາດປະສົມກັນໄຟ	ໂຄໂມໂນຍ 56	EJS02 ຫຼື EJS03	ການຫຸ້ມຫໍ່ທີ່ຮຸກຮານທາງເຄມີ
ໂພລີເມີ ວິສະວະກໍາອຸນຫະພູມສູງ	ໂຄໂມໂນຍ 83	EJS04	EJS04 ທົນທານຕໍ່ເຖິງປະມານ 600 ° C
ເຮັດຄວາມສະອາດ PP, PE, PS, ABS	Nitriding ແມ່ນພຽງພໍ		ບໍ່ມີການຂັດ, ບໍ່ມີການກັດກ່ອນ - ປະຫຍັດເງິນ

5. ໃນເວລາທີ່ມັນຈ່າຍສໍາລັບຕົວມັນເອງ

ຫ້າເງື່ອນໄຂເຮັດໃຫ້ການຍົກລະດັບ. ຫນຶ່ງໃນພວກມັນແມ່ນປົກກະຕິພຽງພໍ.

ເຄື່ອງຕື່ມສານຂັດ.ເສັ້ນໃຍແກ້ວ, ທາດການຊຽມຄາບອນ, talc, ເສີມແຮ່ທາດ. ເຫຼົ່ານີ້ຕັດກໍລະນີ nitride ຄ້າຍຄື sandpaper ຕັດໄມ້ອ່ອນ.
ເຄມີ corrosion.PVC ແຂງແຮງປ່ອຍອອກ HCl ຍ້ອນວ່າມັນ degrades. ການຫຸ້ມຫໍ່ທີ່ທົນທານຕໍ່ໄຟຫຼາຍແມ່ນມີຄວາມຮຸກຮານທາງເຄມີ. fluoropolymers ໂຈມຕີເຫຼັກໂດຍກົງ.
ລີໄຊເຄີນ ແລະອາຫານຫຼັງຜູ້ບໍລິໂພກ.Regrind ປະກອບດ້ວຍ grit, ການປັບໄຫມໂລຫະ, ແລະການປົນເປື້ອນທີ່ບໍ່ສາມາດຄາດເດົາໄດ້ - ວັດສະດຸທີ່ຂັດທີ່ສຸດທີ່ໂຮງງານຜະລິດສ່ວນໃຫຍ່ດໍາເນີນການ.
ກະແສໄຟຟ້າສູງບ່ອນທີ່ເວລາຢຸດເຮັດວຽກເຈັບປວດ.ຖ້າການປ່ຽນແປງສະກູມີຄ່າໃຊ້ຈ່າຍໃນການຜະລິດສາມມື້, ເສດຖະກິດຫັນໄປສູ່ພາກສ່ວນທີ່ຕ້ອງການການປ່ຽນແປງຫນ້ອຍລົງເລື້ອຍໆ.
ປະຫວັດການສວມໃສ່ກ່າວວ່າ nitrided ແມ່ນການເອີ້ນທີ່ບໍ່ຖືກຕ້ອງ.ສ່ວນ nitrided ທີ່ໝົດໄວໃນສານປະສົມຂອງເຈົ້າກຳລັງບອກເຈົ້າບາງຢ່າງ. ການທົດແທນແມ່ນປັດຈຸບັນລາຄາຖືກທີ່ສຸດເພື່ອແກ້ໄຂສະເພາະ.

Bimetallic screw barrel for a plastic recycling extruder where abrasive contamination justifies the upgrade — ຫນ້າທີ່ການລີໄຊເຄີນແມ່ນບ່ອນທີ່ bimetallic ມີລາຍໄດ້ໄວທີ່ສຸດ. Regrind ປະຕິບັດການປັບໄຫມແລະໂລຫະທີ່ຕັດກໍລະນີ nitride ບາງໆຢ່າງໄວວາ.

ກໍລະນີການເປັນເຈົ້າຂອງຄ່າໃຊ້ຈ່າຍທັງຫມົດແມ່ນກົງໄປກົງມາ. Bimetallic ມີລາຄາຖືກກວ່າ. ໃນຫນ້າທີ່ຂັດ, ຊີວິດຂອງຖັງ screw ຂະຫຍາຍຫຼຸດລົງຄ່າໃຊ້ຈ່າຍຕໍ່ຊົ່ວໂມງແລ່ນຕ່ໍາ nitrided, ປົກກະຕິແລ້ວພາຍໃນວົງຈອນການທົດແທນຄັ້ງທໍາອິດ. ຄະນິດສາດທີ່ແນ່ນອນແມ່ນຂຶ້ນກັບຢາງຂອງທ່ານ, ການໂຫຼດຂອງ filler, throughput, ແລະການຢຸດເວລາຫນຶ່ງຊົ່ວໂມງຂອງສາຍຂອງທ່ານ - ເຊິ່ງແມ່ນເຫດຜົນທີ່ວ່າຜູ້ສະຫນອງໃດໆທີ່ອ້າງເຖິງຕົວຄູນຊີວິດທົ່ວໂລກໂດຍບໍ່ໄດ້ຖາມກ່ຽວກັບສານປະສົມຂອງເຈົ້າແມ່ນຄາດເດົາ.

6. ເມື່ອເຈົ້າບໍ່ຄວນຊື້ Bimetallic

ບໍ່ມີຄູ່ແຂ່ງຂຽນພາກນີ້. ອ່ານມັນແນວໃດ — ມັນອາດຈະຊ່ວຍປະຢັດເງິນຂອງທ່ານ.

ຢາງທີ່ສະອາດ, ບໍ່ໄດ້ຕື່ມ, ບໍ່ຈໍາເປັນຕ້ອງ bimetallic.ຖ້າທ່ານດໍາເນີນການ PP, PE, PS, ຫຼື ABS ທໍາມະຊາດໂດຍບໍ່ມີສານຂັດແລະບໍ່ມີສານເພີ່ມ corrosive, screw ແລະ barrel nitrided ໃນ 38CrMoAlA ຈະໃຫ້ບໍລິການທ່ານໄດ້ດີແລະມີລາຄາຖືກກວ່າຫຼາຍ. ການປົກປ້ອງ bimetallic ນັ່ງຢູ່ຊື່ໆ. ທ່ານໄດ້ຈ່າຍສໍາລັບລົດຫຸ້ມເກາະຕໍ່ຕ້ານສັດຕູທີ່ບໍ່ເຄີຍສະແດງໃຫ້ເຫັນເຖິງ.

ເສັ້ນຜ່ານທາງຕ່ຳ ຫຼື ໄລຍະຫ່າງໆ.ຖ້າເຄື່ອງແລ່ນສອງສາມຊົ່ວໂມງຕໍ່ອາທິດ, ການສວມໃສ່ຊ້າລົງໂດຍບໍ່ຄໍານຶງເຖິງການກໍ່ສ້າງ. ໄລຍະເວລາຈ່າຍຄືນໄດ້ຍືດຍາວຜ່ານຈຸດທີ່ມັນມີຄວາມໝາຍ.

ເມື່ອບັນຫາທີ່ແທ້ຈິງແມ່ນສິ່ງອື່ນ.ບາງຄັ້ງການສວມໃສ່ກ່ອນໄວອັນຄວນແມ່ນມາຈາກສະກູທີ່ບໍ່ສອດຄ່ອງ, ແກນງໍ, ການປົນເປື້ອນໃນອາຫານ, ຫຼືຂະບວນການທີ່ເຮັດວຽກສູງກວ່າອຸນຫະພູມຂອງການອອກແບບ. ການກໍ່ສ້າງ bimetallic ຈະບໍ່ແກ້ໄຂສິ່ງເຫຼົ່ານັ້ນ - ມັນພຽງແຕ່ຈະຫມົດໄປຊ້າກວ່າໃນຂະນະທີ່ຄວາມຜິດພື້ນຖານຍັງສືບຕໍ່. ວິເຄາະກ່ອນທີ່ທ່ານຈະຍົກລະດັບ.

ຜູ້ສະຫນອງທີ່ຊື່ສັດຈະບອກທ່ານນີ້. ຖາມຜູ້ຜະລິດວ່າສານປະສົມຂອງເຈົ້າໃຫ້ເຫດຜົນກັບ bimetallic, ແລະເອົາໃຈໃສ່ກັບວ່າພວກເຂົາຖາມສິ່ງທີ່ເຈົ້າແລ່ນຕົວຈິງກ່ອນທີ່ຈະຕອບ.

7. ວິທີການກວດສອບວ່າທ່ານໄດ້ຮັບ Bimetallic ຢ່າງແທ້ຈິງ

ຄໍາວ່າ "bimetallic" ປາກົດຢູ່ໃນໃບແຈ້ງຫນີ້ຈໍານວນຫຼາຍ. ໂລຫະປະສົມບໍ່ສະເຫມີໄປປາກົດຢູ່ໃນສ່ວນ. ສີ່ກວດກາປົກປ້ອງທ່ານ.

ບັນຊີລາຍການກວດສອບ

ຂໍໃຫ້ສໍາລັບຊັ້ນຜະລິດຕະພັນໃນລາຍລັກອັກສອນ, ກ່ຽວກັບວົງຢືມ.ບໍ່ແມ່ນ "ໂລຫະປະສົມທີ່ອີງໃສ່ nickel" — ຊື່ຊັ້ນ. Ni60, Colmonoy 56, Colmonoy 83, ຫຼືການອອກແບບຂອງຕົນເອງຂອງຜູ້ຜະລິດທີ່ມີອົງປະກອບທີ່ຈັດພີມມາ.
ຂໍຄວາມໜາຂອງຊັ້ນໃນການຂຽນ.Screw hardfacing ຄວນ 1.0-1.5 ມມ. ເສັ້ນຜ່າສູນກາງຂອງຖັງຄວນຈະເປັນ 2.0-3.0 ມມ. ຜູ້ສະໜອງທີ່ອ້າງເຖິງ 0.5 ມມ ໃສ່ຖັງກຳລັງຂາຍອັນອື່ນໃຫ້ທ່ານ.
ຮ້ອງຂໍໃບຢັ້ງຢືນວັດສະດຸສໍາລັບເຫຼັກພື້ນຖານ.ທຸກໆ batch ຄວນມີໃບຢັ້ງຢືນການທົດສອບໂຮງງານສະແດງໃຫ້ເຫັນເຄມີສາດແລະຄຸນສົມບັດກົນຈັກ. ກວດເບິ່ງຕົວເລກຄວາມຮ້ອນຂ້າມ.
ໃນຄໍາສັ່ງທໍາອິດ, ມີການວິເຄາະຕົວຢ່າງ.ຫ້ອງທົດລອງໂລຫະສາມາດແຍກຄູປອງແລະຢືນຢັນຄວາມຫນາຂອງຊັ້ນ, ເຄມີຂອງໂລຫະປະສົມ, ແລະຄຸນນະພາບພັນທະບັດ. ຄ່າໃຊ້ຈ່າຍແມ່ນເລັກນ້ອຍຕໍ່ກັບຖັງຂອງ screws.

ຜູ້ຜະລິດທີ່ສ້າງ bimetallic ພາຍໃນເຮືອນໃຫ້ຄໍາຕອບທັງຫມົດສີ່ໂດຍບໍ່ມີການ friction. EJS ສະຫນອງບົດລາຍງານການກວດກາແລະໃບຢັ້ງຢືນວັດສະດຸກັບທຸກໆຖັງ screw, ແລະສະແຕມເລກປະຈໍາຕົວທີ່ສາມາດຕິດຕາມໄດ້ໃນແຕ່ລະພາກສ່ວນໃນລະຫວ່າງການຜະລິດ. ການລັງເລໃນຈຸດໃດນຶ່ງເຫຼົ່ານີ້ແມ່ນສົມຄວນທີ່ຈະສັງເກດເຫັນ.

8. ວິທີການ Spec Quote

Screw barrels ແມ່ນຢູ່ໃກ້ກັບ 100% ພາກສ່ວນ custom. ບໍ່ມີລາຄາໃນລາຍຊື່ - ຜູ້ຜະລິດສ້າງລາຄາຈາກສະເພາະຂອງທ່ານ, ດັ່ງນັ້ນຄຸນນະພາບຂອງການສອບຖາມຂອງເຈົ້າກໍານົດຄຸນນະພາບຂອງຄໍາຕອບ.

ສົ່ງຫົກລາຍການເຫຼົ່ານີ້ແລະລາຄາໂຮງງານທີ່ຮຸນແຮງພາຍໃນຫນຶ່ງມື້ເຮັດວຽກ:

ເຄື່ອງຈັກຜະລິດແລະຮູບແບບ.ຊິ້ນສ່ວນແມ່ນສ້າງຂຶ້ນຕາມຮູບແຕ້ມຫຼືຕໍ່ຍີ່ຫໍ້ເຄື່ອງຈັກແລະລະຫັດ.
ເສັ້ນຜ່າສູນກາງຂອງ screw, ອັດຕາສ່ວນ L / D, ແລະຄວາມຍາວໂດຍລວມ.
ປະສົມຂອງເຈົ້າ, ກ່າວດ້ວຍຄວາມຊື່ສັດ."PP" ແລະ "PP ກັບ 25% talc ບວກ 15% regrind" ແມ່ນບັນຫາການສວມໃສ່ທີ່ແຕກຕ່າງກັນກັບຄໍາຕອບໂລຫະປະສົມທີ່ແຕກຕ່າງກັນ. ເສັ້ນນີ້ເຮັດໃຫ້ຄໍາແນະນໍາດ້ານໂລຫະຫຼາຍກວ່າສິ່ງອື່ນທີ່ທ່ານສົ່ງ.
ຊ່ວງອຸນຫະພູມຂະບວນການ.ຝາອັດປາກຂຸມໂລຫະປະສົມຖັງຢູ່ໃນຂອບເຂດຈໍາກັດທີ່ແຕກຕ່າງກັນ - EJS01 ຢູ່ທີ່ປະມານ 400 ° C, EJS04 ຢູ່ທີ່ປະມານ 600 ° C.
ການແຕ້ມຮູບຖ້າທ່ານມີຫນຶ່ງ.ໂດຍບໍ່ມີການແຕ້ມຮູບ, ສົ່ງຮູບຜະລິດຕະພັນບວກກັບຂະຫນາດທີ່ສໍາຄັນ - ເສັ້ນຜ່າກາງ, ຄວາມຍາວ, ລາຍລະອຽດຂອງຫນ້າຕ່າງ.
ການກໍ່ສ້າງໃຫມ່ຫຼືທົດແທນ?ສໍາລັບການປ່ຽນແທນ, ການວັດແທກການສວມໃສ່ແລະຮູບພາບຂອງສ່ວນທີ່ສວມໃສ່ໃຫ້ໂຮງງານຕັດສິນວ່າການປັບປຸງໃຫມ່ດີກວ່າການຜະລິດໃຫມ່.

EJS ໄດ້ຜະລິດ screws ແລະ barrels ຢູ່ໂຮງງານ Zhoushan ຂອງຕົນນັບຕັ້ງແຕ່ 1992, ແລະກໍ່ສ້າງການກໍ່ສ້າງ bimetallic ພາຍໃນເຮືອນ - ການເຊື່ອມ PTA ສໍາລັບ screws, ການຫລໍ່ centrifugal ສໍາລັບ barrels - ໃນທົ່ວ screw ດຽວ (Ø12-500 mm), ຄູ່ຂະຫນານ, ຄູ່ແຝດຮູບຈວຍ, ການສີດ, ແລະເລຂາຄະນິດຢາງ. ການຜະລິດດໍາເນີນການ 20 ຫາ 70 ມື້ຫຼັງຈາກການຢັ້ງຢືນການແຕ້ມຮູບ, ມີການຮັບປະກັນຫນຶ່ງປີກ່ຽວກັບພາດສະຕິກບໍລິສຸດ.

9. ຄໍາຖາມທີ່ພົບເລື້ອຍ

ຖັງສະກູ bimetallic ເຮັດມາຈາກຫຍັງ?

ຖັງສະກູ bimetallic ປະສົມປະສານກັບຖານເຫຼັກທີ່ມີຊັ້ນໂລຫະປະສົມທີ່ທົນທານຕໍ່ການສວມໃສ່ແຍກຕ່າງຫາກທີ່ຜູກມັດກັບພື້ນຜິວທີ່ເຮັດວຽກ. ເຫຼັກພື້ນຖານທົ່ວໄປປະກອບມີ 38CrMoAlA, 34CrAlNi7, 31CrMoV9, ແລະ 42CrMo. ຊັ້ນໂລຫະປະສົມໃນສະກູແມ່ນປົກກະຕິແລ້ວ Ni60, Colmonoy 56, ຫຼື Colmonoy 83, ນໍາໃຊ້ໂດຍການເຊື່ອມໂລຫະ PTA ທີ່ມີຄວາມຫນາ 1.0 ຫາ 1.5 ມມ. ຊັ້ນໂລຫະປະສົມພາຍໃນຖັງແມ່ນເປັນໂລຫະປະສົມທີ່ອີງໃສ່ nickel- ຫຼືທາດເຫຼັກ, ນໍາໃຊ້ໂດຍການຫລໍ່ centrifugal ຢູ່ທີ່ 2.0 ຫາ 3.0 ມມ. ວັດສະດຸທັງສອງຢູ່ໃນຊັ້ນທີ່ແຕກຕ່າງກັນໂດຍມີໂລຫະປະສົມລະຫວ່າງພວກມັນ.

ຖັງສະກູ bimetallic ໃຊ້ໄດ້ດົນກວ່າ nitrided ຫຼາຍເທົ່າໃດ?

ດົນພໍທີ່ຈະສຳຄັນກັບສານຂັດ, ແລະບໍ່ດົນພໍທີ່ຈະສຳຄັນກັບສິ່ງທີ່ສະອາດ. ໃນອາຫານທີ່ເຕັມໄປດ້ວຍແກ້ວ, ແຮ່ທາດ, ຫຼືລີໄຊເຄີນ, ຄວາມແຕກຕ່າງຂອງຊີວິດການບໍລິການແມ່ນຢ່າງຫຼວງຫຼາຍ, ເພາະວ່າກໍລະນີ nitride ມີຄວາມເລິກພຽງແຕ່ 0.4 ຫາ 0.7 ມມ, ໃນຂະນະທີ່ bimetallic ໃຫ້ 1.0 ຫາ 1.5 ມມໃນສະກູແລະ 2.0 ຫາ 3.0 ມມໃນຖັງ, ໃນອຸປະກອນທີ່ແຂງແລະທົນທານຕໍ່ສານເຄມີຫຼາຍ. ໃນຢາງທີ່ສະອາດທີ່ບໍ່ໄດ້ເຕີມເຕັມ, ການກໍ່ສ້າງທັງສອງສາມາດດໍາເນີນໄປເປັນປີແລະການຍົກລະດັບມີລາຍໄດ້ຫນ້ອຍ. ຜູ້ສະໜອງໃດໆກໍຕາມທີ່ອ້າງເຖິງຕົວຄູນຄົງທີ່ໂດຍບໍ່ໄດ້ຖາມສິ່ງທີ່ເຈົ້າປະມວນຜົນແມ່ນເດົາ.

ຖັງສະກູ bimetallic ຄືກັນກັບແຜ່ນທີ່ມີ chrome ບໍ?

ບໍ່. ແຜ່ນ Chrome ຝາກຊັ້ນບາງໆຢູ່ເທິງພື້ນຜິວ, ເຊິ່ງສາມາດແຕກອອກພາຍໃຕ້ວົງຈອນຄວາມຮ້ອນແລະການໂຫຼດກົນຈັກ. ການກໍ່ສ້າງ bimetallic fuses ຫຼາຍ millimeters ຂອງໂລຫະປະສົມກັບເຫຼັກພື້ນຖານໂດຍຜ່ານການເຊື່ອມຫຼືຫລໍ່, ດັ່ງນັ້ນຊັ້ນໄດ້ກາຍເປັນສ່ວນຫນຶ່ງຂອງອົງປະກອບແລະບໍ່ສາມາດປອກເປືອກໄດ້. ແຜ່ນ Chrome ໃຫ້ບໍລິການຈຸດປະສົງສະເພາະເຊັ່ນ: ການປ່ອຍແລະການປ້ອງກັນການກັດກ່ອນເລັກນ້ອຍ, ແຕ່ມັນບໍ່ແມ່ນການແກ້ໄຂການສວມໃສ່ສໍາລັບທາດປະສົມທີ່ຂັດ.

ສະກູ bimetallic ສາມາດສ້ອມແປງໄດ້ເມື່ອມັນສວມອອກບໍ?

ແມ່ນແລ້ວ, ໃນຫຼາຍໆກໍລະນີ. ສະກູ bimetallic ທີ່ສວມໃສ່ສາມາດຖືກເຊື່ອມຄືນໃຫມ່ດ້ວຍການຫັນຫນ້າ PTA ສົດໆແລະເຄື່ອງຈັກກັບຄືນສູ່ເລຂາຄະນິດເດີມ. ການເຈາະຖັງທີ່ສວມໃສ່ສາມາດຖືກເຈາະຄືນໃຫມ່ແລະວາງສາຍໃຫມ່ໂດຍການຫລໍ່ດ້ວຍແຮງດັນ. ການປັບປຸງໃຫມ່ຮັກສາ shaft ຕົ້ນສະບັບ, keyway, ວາລະສານ, ແລະທີ່ຢູ່ອາໄສ, ເຊິ່ງມັກຈະເຮັດໃຫ້ມັນເປັນເສັ້ນທາງປະຫຍັດໃນເວລາທີ່ພາກສ່ວນ OEM ຢຸດເຊົາຫຼືເວລານໍາແມ່ນຍາວ. ສົ່ງຮູບແລະການວັດແທກໃສ່ເພື່ອໄດ້ຮັບການປະເມີນຄືນໃຫມ່ຫຼືປ່ຽນແທນ.

ຂ້ອຍຕ້ອງການ bimetallic ສໍາລັບ screw, barrel, ຫຼືທັງສອງ?

ທັງສອງ, ໃນກໍລະນີຫຼາຍທີ່ສຸດ, ເພາະວ່າພວກເຂົາໃສ່ເປັນຄູ່. ການເກັບກູ້ລະຫວ່າງທີ່ດິນການບິນແລະເຈາະແມ່ນຊັບສິນລະບົບ. screw bimetallic ໃໝ່ ພາຍໃນຂຸມທີ່ມີຂະຫນາດໃຫຍ່ທີ່ສວມໃສ່ຍັງແລ່ນຢູ່ໃນການຂະຫຍາຍໃຫຍ່ຂື້ນ, ດັ່ງນັ້ນຜົນຜະລິດຈະຢູ່ໃນລະດັບຕໍ່າແລະສະກູໃຫມ່ຈະສວມໃສ່ກັບພື້ນຜິວທີ່ບໍ່ສະຫມໍ່າສະເຫມີ. ຖ້າທ່ານກໍາລັງຍົກລະດັບຫນຶ່ງ, ໃຫ້ວັດແທກອີກອັນຫນຶ່ງ. ການທົດແທນພຽງແຕ່ເຄິ່ງຫນຶ່ງຂອງຄູ່ສວມໃສ່ຈະໂອນບັນຫາໄປສູ່ສ່ວນໃຫມ່.

ຖັງ screw bimetallic ເຮັດວຽກສໍາລັບ PVC ບໍ?

ແມ່ນແລ້ວ, ແຕ່ຊັ້ນຂອງໂລຫະປະສົມມີຄວາມສໍາຄັນຫຼາຍກ່ວາປ້າຍຊື່. PVC ແຂງແມ່ນບັນຫາ corrosion ກ່ອນທີ່ຈະເປັນບັນຫາການຂັດ, ເນື່ອງຈາກວ່າໂພລີເມີປ່ອຍ hydrogen chloride ຍ້ອນວ່າມັນ degrades. ນັ້ນຫມາຍຄວາມວ່າທ່ານຕ້ອງການໂລຫະປະສົມທີ່ນໍາພາການກັດກ່ອນ: Ni60 ຫຼື Colmonoy 56 ໃນສະກູ, ແລະ EJS02 ຫຼື EJS03 ໃນຖັງ. ເກຣດ tungsten-carbide ເຊັ່ນ Colmonoy 83 ຖືກສ້າງຂຶ້ນສໍາລັບການຂັດແລະບໍ່ແມ່ນຄໍາຕອບທີ່ຖືກຕ້ອງສໍາລັບ PVC ເວັ້ນເສຍແຕ່ວ່າສານປະກອບປະກອບດ້ວຍສານເຕີມເຕັມທີ່ຫນັກແຫນ້ນເຊັ່ນກັນ.

ຂີດຈຳກັດອຸນຫະພູມຂອງຖັງ bimetallic ແມ່ນຫຍັງ?

ມັນຂຶ້ນກັບໂລຫະປະສົມການຫລໍ່, ແລະມັນມີລະດັບຈາກປະມານ 400 ຫາ 600 ອົງສາເຊນຊຽດ. EJS01 ຖືກຈັດອັນດັບປະມານ 400. EJS02 ແລະ EJS03 ບັນລຸປະມານ 450. EJS04, ເກຣດ tungsten carbide, ທົນທານໄດ້ເຖິງປະມານ 600. ຖ້າຂະບວນການຂອງທ່ານຮ້ອນ, ຂອບເຂດຈໍາກັດຂອງອຸນຫະພູມຈະກາຍເປັນຕົວກໍານົດການ gating, ສະນັ້ນບອກຜູ້ຜະລິດຂອງທ່ານກ່ຽວກັບອຸນຫະພູມເຂດຕົວຈິງແທນທີ່ຈະເປັນມູນຄ່າການອອກແບບ.

EJS ສາມາດສະຫນອງຖັງ screw bimetallic ສໍາລັບເຄື່ອງຈັກຂອງຂ້ອຍບໍ?

ແມ່ນແລ້ວ. EJS ຜະລິດ screws bimetallic ແລະ barrels ພາຍໃນເຮືອນ, ມີ PTA-welded hardfacing ສຸດ screws ແລະ centrifugally cast lining ໃນ barrels, ສໍາລັບ screw ດຽວ, ຄູ່ຂະຫນານ, ຝາແຝດ conical, ການສີດ, ແລະເລຂາຄະນິດຢາງ. ຊິ້ນສ່ວນຕ່າງໆແມ່ນສ້າງຂຶ້ນຕາມຮູບແຕ້ມ ຫຼື ເຄື່ອງຈັກແບບປີ້ນກັບກັນຈາກຕົວແບບເຄື່ອງຈັກ ແລະ ລະຫັດເມື່ອບໍ່ມີຮູບແຕ້ມ. ວົງຢືມປະຕິບັດຕາມພາຍໃນຫນຶ່ງມື້ເຮັດວຽກເມື່ອຂໍ້ກໍາຫນົດຈະແຈ້ງ.

ຖັງ Screw Bimetallic ແມ່ນຫຍັງ? (ແລະເມື່ອມັນຄຸ້ມຄ່າ)